Product name：Ceramic Enhancer
Item no：HJ-CSP-01
CAS NO: 371120171118064760
Technical data：
Product appearance: white powder
Chemical composite:
|
Item |
Elements |
Result（%） |
Item |
Elements |
Result（%） |
|
1 |
IL |
21.12 |
13 |
Li2O |
0.01 |
|
2 |
Al2O3 |
0.04 |
14 |
PbO |
0.01 |
|
3 |
SIO2 |
2.14 |
15 |
ZnO |
0.01 |
|
4 |
Fe2O3 |
0.01 |
16 |
MnO2 |
0.01 |
|
5 |
CaO |
0.21 |
17 |
CoO |
0.01 |
|
6 |
MgO |
0.034 |
18 |
NiO |
0.01 |
|
7 |
K2O |
0.038 |
19 |
CuO |
0.01 |
|
8 |
Na2O |
44.46 |
20 |
Cr2O3 |
0.01 |
|
9 |
TiO2 |
0.01 |
21 |
SO3 |
0.04 |
|
10 |
SrO |
0.01 |
22 |
B2O3 |
31.77 |
|
11 |
BaO |
0.01 |
|
|
|
|
12 |
CeO2 |
0.01 |
|
|
|
Package：25KG / bag
Storage method and precautions: sealed in a plastic bag and stored in a dry and cool place.
Application features:
1）Easily soluble in water, the solution has no viscosity and has degumming properties. After adding the mud, it has no effect on the flow rate of the mud. At the same time, it reduces the water content of the mud and saves energy consumption of the spray drying tower.
2）Good solubility, can be ground together with mud or external mixing and stirring can achieve the using effect.
3）The product will not rot when it is added to the mud for a long time, and it will not fail if the time exceeds 24 hours. Reduces the thixotropy of the mud, and makes the mud smoother and transport smoother.
4）It can replace the increasingly scarce clay, reduce the amount of bricks, and save a lot of costs. Each addition of 0.3% will reduce the clay by 3% and its strength is greater than lignin.
5）After replacing the plastic clay, the strength of the green body can be significantly increased. After the addition, the overall brick will be significantly improved, and the colorant proportion is saved.
6）Improve the flatness of the glazed surface after glazing, and evenly penetrate the green body after glazing to reduce the generation of pinhole concave glaze.
7）Due to the reduction of clay, the burning loss of plastic clay is reduced, and the brick can be burned at a low temperature, which can increase the yield of the kiln and save the fuel cost; and because the moisture of the clay mud is less volatile, reducing the amount of clay, reduce the defects of the blank surface and even the glaze, and reduce the occurrence of pinhole-like phenomena.
8）It is a very good material in the production of ceramic tiles, and it has a significant effect on the reinforcement of the green body, which can greatly reduce the problem of cracking and damage in the production process.
9）Because less clay is added, after adjusting the formula structure, energy costs can be saved; the moisture in the mud can be reduced; (the moisture content of the dusting powder can be reduced); the manufacturing cost and the expansion coefficient of the green body can be reduced.